200℃ ~600℃ Organic Silicon  Aluminum power High Temperature Finish

200℃ ~600℃ Organic Silicon Aluminum power High Temperature Finish

200℃ ~600℃ Organic Silicon Aluminum power High Temperature Finish

一,400℃Organic Silicon Aluminum power High Temperature Finish

Characteristics:excellent heat resistance、elements resistance property, perfect construction property.
Uses:applicable for sprayed under 400℃ steel and other high temperature parts, play a role of heat resistance protection and anticorrosion.
Technical target:
Mixing ratio: double component: paint/aluminum paste=17/3
Standard film thickness: Dry: 25μm/coat
Academic spreading rate: 0.09kg/ m2/25μm
Solid contents: 35%
Humidity requirement: below 85%
Drying time & Coating interval

Temperature(℃)

-10

0

10

20

30

Dry to touch(hrs)

60

50

40

30

20

Dry semi-hard(hrs)

12

8

6

5

4

Min. interval(hrs)

12

8

6

5

4

Substrate treatment:Primer surface should be clean and dry, no feculence
Matching :Applicable under coatings: FX400℃ organic silicon heat resistance primers

二,200℃Organic Silicon Aluminum Powder High Temperature Finish

Characteristics:dry quickly, excellent physical and mechanical property、perfect heat resistance、elements resistance, good construction property.
Uses:applicable for sprayed under 200℃ steel and other high temperature parts, play a role of heat resistance protection and anticorrosion.
Technical target:
Mixing ratio: double component paint/aluminum paste=17/3
Standard film thickness: Dry: 25μm/coat
Academic spreading rate: 0.09kg/ m2/25μm
Solid contents: 35%
Humidity requirement: under 85%
Drying time & Coating interval

Temperature(℃)

-10

0

10

20

30

Dry to touch(hrs)

60

50

40

30

20

Dry semi-hard(hrs)

12

8

6

5

4

Min. interval(hrs)

12

8

6

5

4

Substrate treatment:Primer surface should be clean and dry, no feculence
Matching:Applicable under coatings: FX200℃ organic silicon heat resistance primers

三, 300℃Organic Silicon Aluminum Powder High Temperature Finish

Characteristics:excellent heat resistance、elements resistance, perfect construction property.
Uses:applicable for sprayed under 300℃ steel and other high temperature parts, play a role of heat resistance protection and anticorrosion.
Technical target:
Mixing ratio: double component paint/aluminum paste=17/3
Standard film thickness: Dry: 25μm/coat
Academic spreading rate: 0.09kg/ m2/25μm
Solid contents: 35%
Humidity requirement: under 85%
Drying time & Coating interval

Temperature(℃)

-10

0

10

20

30

Dry to touch(hrs)

60

50

40

30

20

Dry semi-hard(hrs)

12

8

6

5

4

Min. interval(hrs)

12

8

6

5

4

Substrate treatment:Primer surface should be clean and dry, no feculence
Matching: Applicable under coatings: FX300℃ organic silicon heat resistance primers

四, 600℃Organic Silicon Aluminum Powder High Temperature Finish

Characteristics:excellent heat resistance、elements resistance、 construction property.
Uses:applicable for sprayed under 600℃ steel and other high temperature parts, play a role of heat resistance protection and anticorrosion.
Technical target:
Mixing ratio: double component paint/aluminum paste=17/3
Standard film thickness: Dry: 25μm/coat
Academic spreading rate: 0.09kg/ m2/25μm
Solid contents: 36%
Humidity requirement: below 85%
Drying time & Coating interval

Temperature(℃)

-10

0

10

20

30

Dry to touch(hrs)

60

50

40

30

20

Dry semi-hard(hrs)

12

8

6

5

4

Min. interval(hrs)

12

8

6

5

4

Substrate treatment:Primer surface should be clean and dry, no feculence
Matching:Applicable under coatings: FX600℃ organic silicon heat resistance primers

CONTACT WITH US NOW