200℃~600℃ Organic Silicon Heat Resistance Primers

200℃~600℃ Organic Silicon Heat Resistance Primers

一, 200℃Organic Silicon Heat Resistance Primers (Grey)

Characteristics:dry quickly, excellent physical and mechanical property、perfect heat resistance、good construction property.
Uses:applicable for sprayed under 200℃ steel and other high temperature parts, play a role of heat resistance protection and anticorrosion.
Technical target:
Mixing ratio: single component
Standard film thickness: Dry: 30μm/coat
Academic spreading rate: 0.10kg/ m2/30μm
Solid contents: 58%
Humidity requirement: under 85%
Drying time & Coating interval

Temperature（℃）	-10	0	10	20	30
Dry to touch（hrs）	50	40	30	20	15
Dry semi-hard（hrs）	10	6	5	3.5	3
Min. interval（hrs）	10	6	5	3.5	3

Substrate treatment:Remove rust and oxide skin by abrasive blasting,reached ISO Sa2.5 grade or handle the surface by electric tools, reached St3 grade
Matching:
Applicable substrate: Unpainted steel
Applicable upper coatings: FX200℃ organic silicon air drying finish and aluminum powder finish

二, 300℃Organic Silicon Heat Resistance Primers(Grey)

Characteristics:dry quickly, excellent physical and mechanical property、perfect heat resistance, good construction property.
Uses:applicable for sprayed under 300℃ steel and other high temperature parts, play a role of heat resistance protection and anticorrosion.
Technical target:
Mixing ratio: single component
Standard film thickness: Dry: 30μm/coat
Academic spreading rate: 0.10kg/ m2/30μm
Solid contents: 58%
Humidity requirement: under 85%
Drying time & Coating interval

Temperature（℃）	-10	0	10	20	30
Dry to touch（hrs）	50	40	30	20	15
Dry semi-hard（hrs）	10	6	5	3.5	3
Min. interval（hrs）	10	6	5	3.5	3

Substrate treatment:Remove rust and oxide skin by abrasive blasting,reached ISO Sa2.5 grade or handle the surface by electric tools, reached St3 grade
Matching :
Applicable substrate: Unpainted steel
Applicable upper coatings: FX300℃ organic silicon air drying finish and aluminum powder finish

三, 400℃Organic Silicon Heat Resistance Primers(Grey)

Characteristics:dry quickly, excellent physical and mechanical property、good heat resistance property、construction property.
Uses:applicable for sprayed under 400℃ steel and other high temperature parts, play a role of heat resistance protection and anticorrosion.
Technical target:
Mixing ratio: single component
Standard film thickness: Dry: 30μm/coat
Academic spreading rate: 0.10kg/ m2/30μm
Solid contents: 58%
Humidity requirement: below 85%
Drying time & Coating interval

Temperature（℃）	-10	0	10	20	30
Dry to touch（hrs）	50	40	30	20	15
Dry semi-hard（hrs）	10	6	5	3.5	3
Min. interval（hrs）	10	6	5	3.5	3

Substrate treatment:Remove rust and oxide skin by abrasive blasting,reached ISO Sa2.5 grade or handle the surface by electric tools, reached St3 grade
Matching:
Applicable substrate: Unpainted steel
Applicable upper coatings: FX400℃ organic silicon air drying finish and aluminum powder finish

四, 600℃Organic Silicon Heat Resistance Primers (Grey)

Characteristics:dry quickly, excellent physical and mechanical property、good heat resistance、construction property.
Uses:applicable for sprayed under 600℃ steel and other high temperature parts, play a role of heat resistance protection and anticorrosion.
Technical target:
Mixing ratio: single component
Standard film thickness: Dry: 30μm/coat
Academic spreading rate: 0.10kg/ m2/30μm
Solid contents: 50%
Humidity requirement: below 85%
Drying time & Coating interval

Temperature（℃）	-10	0	10	20	30
Dry to touch（hrs）	50	40	30	20	15
Dry semi-hard（hrs）	10	6	5	3.5	3
Min. interval（hrs）	10	6	5	3.5	3

Substrate treatment:Remove rust and oxide skin by abrasive blasting,reached ISO Sa2.5 grade or handle the surface by electric tools, reached St3 grade
Matching :
Applicable substrate: Unpainted steel
Applicable upper coatings: FX600℃ organic silicon air drying high temperature finish and aluminum powder finish