Epoxy Linking Paint

Epoxy Linking Paint

Epoxy Linking Paint(use for bridge and shipping boat)


Characteristics:excellent flexility、shielding, low water permeability, dry property in low temperature, it can still be firmed under -10℃, perfect adhesion with nonferrous metal.
Uses:Mainly use for transitional coupling of bilge antifouling paint,also can use for nonferrous metal surface, as a use of transitional primers.


Technical target:
Mixing ratio: Host crystal/Firming agent=8/1(by weight)
Standard film thickness: Dry: 40μm/coat
Academic spreading rate: 0.12kg/ m2/40μm
Solid contents: 67%
Humidity requirement: below 85%


Drying time & Coating interval

Temperature℃

-10

0

10

20

30

Dry to touch (hrs)

4

2.5

2

1.5

1

Dry semi-hard (hrs)

36

24

18

12

10

Min. interval (hrs)

36

24

18

12

10

Substrate treatment:Unpainted steel surface must abrasive blasting and remove rust, reached ISO Sa2.5 grade, aluminum material、zinc material surface should be clean、dry、no feculence and remove zinc salt, primers surface must dry、no feculence
Matching:
Applicable substrate: unpainted steel、zinc material、aluminum material or sprayed kinds of zinc powder paints and surface of bilge anticorrosive paint
Applicable upper coatings: kinds of polyurethane、epoxy or bilge antifouling paint、chlorination rubber paint etc.