JQ.SJ101C Fluoride-basic Type Sintered Flux

JQ.SJ101C Fluoride-basic Type Sintered Flux

JQ.SJ101C
GB:F4A4-H08MnA F5A4-H10Mn2
AWS:F6A4-EM12
Current:If used together with appropriate wires (such as H08MnA, H10Mn2, etc.), they can be used for welding hull structures, and also used for welding some key structures like boilers, pressure vessels, pipelines, etc.
Main Applications:

JQ.SJ101C

According with GB F4A4-H08MnA F5A4-H10Mn2
Corresponding with AWS F6A4-EM12
DIN BF B165AC12MHP5


Introduction: JQ.SJ101C is a kind of fluoride-basic type sintered flux for ships. The alkalinity is approximately 1.8. Gray round grains. The granularity is 2.0~0.28mm (10~60 meshes/inch). It has excellent welding performance, complete metallurgical reactions, stable arc, good slag detachability and beautiful appearance of weld. The deposited metal has higher low temperature impact toughness. AC/DC. When welding with direct current, the wire should be connected to the positive terminal.


Uses: If used together with appropriate wires (such as H08MnA, H10Mn2, etc.), they can be used for welding hull structures, and also used for welding some key structures like boilers, pressure vessels, pipelines, etc.


Reference Composition of Flux(%)
S
P
SiO2+TiO2
CaO+MgO
Al2O3+MnO
CaF2
≤0.06
≤0.08
15~25
25~35
20~30
15~25

Mechanical Properties of Deposited Metal
Items Rm ReL或Rp0.2 A KV2(J)
Flux Used Together (Mpa) (Mpa) (%) -20℃
H08MnA 410-550 ≥330 ≥22 ≥34
H10Mn2 450~600 ≥375 ≥22 ≥34

Instructions:
1.The fluxes should be baked under 300~350℃ for 2 hours before using.
2.The stains on the weldments, such as rust, oil stains, moisture, etc., must be cleared away before welding.