Acrylic Acid Modified Chlorinated Polyvinyl Chloride Anticorrosive Finish

Acrylic Acid Modified Chlorinated Polyvinyl Chloride Anticorrosive Finish (Different Colors) (Use for steel structure)

Characteristics:paint film dry quickly, excellent resistance of corrosion and moist property, good chemicla resistance property, resistance of spread burning, it can be stilled constructed in -20℃
Uses:applicable for chemical machinery、equipment、pipeline etc. metal, anticorrosive coating of cement part, anticorrosion of acid、 alkali and chemical medicine.
Technical target：
Mixing ratio: single component
Standard film thickness: Dry: 30μm/coat
Academic spreading rate: 0.11kg/ m2/30μm
Solid contents: 40%
Humidity requirement: below 85%
Drying time & Coating interval

Temperature（℃）	0	10	20	30
Dry to touch（hrs）	30	20	15	10
Dry semi-hard（hrs）	4	3	1.5	1
Min. interval（hrs）	10	9	7	5

Substrate treatment：Primers(intermediate paint)surface should be clean and dry, no feculence. Sweep remove dust etc. feculence by pressure-air. If construction environment humidity ＞70%, add measured FX-2 chlorinated polyvinyl chloride damp-proofing admixture.
Matching：Applicable substrate:Substrate which sprayed chlorinated polyvinyl chloride primer