High Chlorinated Polyethylene Anticorrosive Paint

High Chlorinated Polyethylene Anticorrosive Primers(use for steel structure)

Characteristics:dry quickly, excellent physical and mechanical property、water resistance、resistance of acid-base corrosion property, construction property, it can still construct in -20℃.
Uses:mainly use for anticorrosion of petrochemical equipment、 pipeline、concrete construction etc. which erode by petrochemical atmosphere environment. Also use for railway、bridge、high tension transmission line、offshore drilling and oil production facilities, kinds of vehicle chassis、heavy machinery.
Technical target:
Mixing ratio: single component
Standard film thickness: Dry: 30μm/coat
Academic spreading rate: 0.11kg/ m2/30μm
Solid contents: 61%
Humidity requirement: below 85%
Drying time & Coating interval

Substrate treatment:Remove rust and oxide skin by abrasive blasting, reached ISO Sa2.5 grade or handle surface by electric tools,reached St3 grade
Matching :
Applicable substrate:Unpainted steel
Applicable upper coatings:
High Chlorinated Polyethylene Anticorrosive Intermediate Paint
High Chlorinated Polyethylene Anticorrosive Finish(Different Colors)

High Chlorinated Polyethylene Anticorrosive Intermediate Paint (use for steel structure)

Characteristics:dry quickly, excellent physical and mechanical property、water resistance、anticorrosion、 resistance of acid-base property, resistance of elements、construction property, it can still construct in -20℃.
Uses:mainly use for anticorrosion of petrochemical equipment、 pipeline、concrete construction etc. which erode by petrochemical atmosphere environment. Also use for railway、bridge、high tension transmission line、offshore drilling and oil production facilities, kinds of vehicle chassis、heavy machinery.
Technical target:
Mixing ratio: single component
Standard film thickness: Dry: 35μm/coat
Academic spreading rate: 0.12kg/ m2/35μm
Solid contents: 65%
Humidity requirement: below 85%
Drying time & Coating interval

Substrate treatment:Primer surface should be clean and dry, no feculence
Matching :
Applicable under coatings: High Chlorinated Polyethylene Anticorrosive Primers
Applicable upper coatings: High Chlorinated Polyethylene Anticorrosive Finish(different colors)

High Chlorinated Polyethylene Anticorrosive Finish (different colors) (use for steel structure)

Characteristics:dry quickly, excellent physical and mechanical property、water resistance、resistance of acid-base corrosion property, resistance of elements、construction property, it can still construct in -20℃.
Uses:mainly use for anticorrosion of petrochemical equipment、 pipeline、concrete construction etc. which erode by petrochemical atmosphere environment. Also use for railway、bridge、high tension transmission line、offshore drilling and oil production facilities, kinds of vehicle chassis、heavy machinery.
Technical target:
Mixing ratio: single component
Standard film thickness: Dry: 30μm/coat
Academic spreading rate: 0.11kg/ m2/30μm
Solid contents: 58%
Humidity requirement: below 85%
Drying time & Coating interval

Substrate treatment:Primer or intermediate paint surface should be clean and dry, no feculence
Matching: Applicable under coatings High Chlorinated Polyethylene Anticorrosive Intermediate Paint, High Chlorinated Polyethylene Anticorrosive Primers