JQ.YJ601Ni1.5-1 Gas-shielded Flux-cored Welding Wire

JQ.YJ601Ni1.5-1

GB：E551T1-K2
AWS：E81T1-K2
Current：Used for welding structures made of 590MPa low-alloy high strength steel. Widely used for welding some key structures like hoisting machinery, bridges, storage tanks, steel-frame structures, etc.
Main Applications：

JQ.YJ601Ni1.5-1

According with GB/T 17493-1998 E551T1-K2
Corresponding with AWS A5.29 E81T1-K2
JIS Z3313 YFL-C506R

Introduction: JQ.YJ601Ni1.5-1 is a kind of titania type CO2 gas-shielded flux-cored welding wire. It has excellent welding performance, soft and stable arc, fewer spatters, good slag detachability and beautiful appearance of weld. All-position welding. It has high welding efficiency. The weld metal has been given toughening treatment by microelements, so it has excellent low temperature toughness above -30℃ and good crack-resistance.

Uses: Used for welding structures made of 590MPa low-alloy high strength steel. Widely used for welding some key structures like hoisting machinery, bridges, storage tanks, steel-frame structures, etc.

Chemical Composition of Deposited Metal (%)(CO₂Shielding Gas)

Chemical Composition	C	Mn	Si	S	P	Ni	Mo	Cr	V
Guarantee Value	≤0.15	0.50-1.75	≤0.80	≤0.030	≤0.030	1.00-2.00	≤0.35	≤0.15	≤0.05
General Result	0.04	1.35	0.35	0.011	0.016	1.50	-	-	-

Mechanical Properties of Deposited Metal

Test Item	R_m(MPa)	R_eL或R_p0.2(Mpa)	A(%)	KV₂(J)
Guarantee Value	≥550	≥470	≥19	≥27（-30℃）
General Result	620	540	26	110

Reference Current (DC+)

Wire Diameter(mm)		φ1.2	φ1.4	φ1.6
Current Range(A)	Downhand Welding	120～300	150～400	180～450
	Vertical Upward Welding and Overhead Position Welding	120～260	150～270	180～280
	Vertical Downward Welding and Overhead Position Welding	200～300	220～300	250～300
	Horizontal Welding	120～280	150～320	180～350

Instructions:
1.The oil stains and rust on the weldments should be cleared away.
2.When welding, the gas flow rate is generally 20～25L/min.
3.When welding with flux-cored welding wires, the extension elongation should be 15～25mm.
4.The humidity of the welding wire storerooms should be preserved below 60%.
5.It is not suitable for non-vacuum-packed welding wires to be stored for more than half a year, and it is not suitable for vacuum-packed welding wires to be stored for more than a year.