Moisturecuring Epoxy Mica Iron Intermediate Coat,Moisturecuring Epoxy Mica Iron Intermediate Coat manufacturer. - Hi-Sea Group 
Moisturecuring Epoxy Mica Iron Intermediate Coat

Moisturecuring Epoxy Mica Iron Intermediate Coat

Moisturecuring Epoxy Mica Iron Intermediate Coat


Characteristics:When air humidity reached 94%, it can still firmed be film normally, physical and chemical property unchangeable, dry quickly, excellent compatibility with kinds of zinc and epoxy powder, good shielding property.
Uses:Mainly use for anticorrosion of steel structure in hige humidity area and anticorrosion of offshore platform、cabin、ballast tank etc. in hige humidity area.


Technical target:
Mixing rate: Host crystal/Firming agent=8/1 (by weight)
Standard film thickness: Dry: 50μm/coat
Academic spreading rate: 0.13kg/ m2/50μm
Solid contents: 77%
Humidity requirement: below 94%


Drying time & Coating interval

Temperature℃

-10

0

10

20

30

Dry to touch (hrs)

3

2

1.5

1.2

1

Dry semi-hard (hrs)

36

24

16

11

9

Min. interval (hrs)

36

24

16

11

9

Substrate treatment:Remove zinc salt and other contaminant on primer surface.
Matching:
Applicable substrate: Zinc powder primer、Epoxy primer
Applicable upper coatings: Compatible with kinds of finishes